ROUND BAR COPPER
Cu-ETP (CW004A) | CuCr1Zr (CW106C)

✔ standard | ✚ non standard, stock availble

cast size (mm)	Cu-ETP (CW004A)	CuCr1Zr (CW106C)	approx kg/m
5	✔		0,2
6	✔		0,3
8	✔	✔	0,5
10	✔	✔	0,7
12	✔	✔	1,0
13		✔	1,2
14	✔	✔	1,4
15	✔	✔	1,6
16	✔	✔	1,8
18	✔	✔	2,3
cast size (mm)	Cu-ETP (CW004A)	CuCr1Zr (CW106C)	approx kg/m
19		✔	2,6
20	✔	✔	2,8
22	✔	✔	3,4
25	✔	✔	4,4
28	✔	✔	5,5
30	✔	✔	6,4
32	✔	✔	7,2
35	✔	✔	8,7
40	✔	✔	11,4
cast size (mm)	Cu-ETP (CW004A)	CuCr1Zr (CW106C)	approx kg/m
45	✔	✔	14,0
50	✔	✔	17,5
55	✔	✔	21,1
60	✔	✔	25,2
65	✔	✔	29,5
70	✔	✔	34,3
71	✔		35,2
75	✔		40,0
80	✔	✔	45,2
cast size (mm)	Cu-ETP (CW004A)	CuCr1Zr (CW106C)	approx kg/m
90	✔	✔	56,6
100	✔	✔	69,0
110	✔		85,0
120	✔		101,0
130	✔		118,0
140	✔		137,0
150	✔		157,3
160	✔		178,9
200	✔		280,0
✔ standard \| ✚ non standard, stock availble 2024-04-08 07:35

Cu-ETP (CW004A) | E-Cu57

	EN	DIN
Alloy	Cu-ETP	E-Cu57
		roodkoper
Standard	EN 13601, EN 12165	DIN 1787
Alloy number	CW004A	2.0060

Chemical composition

Cu	≥ 99,90	≥ 99,90
Oxygen	0,040 max.	0,040 max.

kg/dm³	ca. 8,9
Characteristics	Oxidized copper with an electrical conductivity of at least 58 m/ohm.mm²

	EN	DIN
Alloy	CuCr1Zr	CuCrZr
Standard	EN 12163, 12167	DIN 17666, 17672
Alloy number	CW106C	2.1293

Chemical composition

Cu	rest	rest
Cr	0,5 - 1,2	0,3 - 1,2
Zr	0,03 - 0,3	0,03 - 0,3

kg/dm³	ca. 8,9
Characteristics	CuCr1Zr has extremely high electrical and thermal conductivity and is resistant to high temperatures. CuCr1Zr is for instance used for resistance welding and electrical equipment components. The termal conductivity at 20 °C is 167 till 320 W/m K abd the electrical conductivity at 20 °C from 26 till m/ohm.mm². CuCr1Zr has a good wear resistance.

	EN	EN	DIN
Alloy	Cu-PHC	Cu-HCP	SE-Cu
Standard	EN 13601	EN 13601, EN 12165	DIN 1787
Alloy number	CW020A	CW021A	2.0070

Chemical composition

Cu	≥ 99,95	≥ 99,95	≥ 99,90
P	0,002 - 0,007	0,002 - 0,007	= 0.003

kg/dm³	ca. 8,9
Characteristics	Oxygen-free copper, deoxidized with phosphorus with a high electrical conductivity. Contains a low residual of phosphorus. Mainly used in the electro- technical industries.

	EN	DIN
Alloy	Cu-DHP	SF-Cu
Standard	EN 12165	DIN 1787
Alloy number	CW024A	2.0090

Chemical composition

Cu	≥ 99,90	≥ 99,90
P	0,015 - 0,040	0,015 - 0,040

kg/dm³	ca. 8,9
Characteristics	Oxygen-free copper, deoxidized witih phosphorus. Contains a low residual of phosphorus. Mainly used in construction industry and machine building

	EN	DIN
Alloy	CuNi2Si	CuNi2Si
Standard	EN 12163, 12165	DIN 17666, 17672
Alloy number	CW111C	2.0855

Chemical composition

Cu	rest	rest
Ni	1,6 - 2,5	1,6 - 2,5
Si	0,4 - 0,8	0,5 - 0,8
Mn	0,8 max.	rest

kg/dm³	ca. 8,8
Characteristics	CuNi2Si offers a high electrical conductivity and tensile strength. CuNi2Si is for instance used as core and ejector pins in the mould industry. The termal conductivity at 20 °C is 67 till 120 W/m.K and the electrical conductivity at 20 °C from 10 till 23 m/ohm.mm².

	EN	DIN
Alloy	CuCo2Be	CuCo2Be
Standard	EN 12163, 12165	DIN 17666, 17672
Alloy number	CW104C	2.1285

Chemical composition

Cu	rest	rest
Co	2,0 - 2,8	2,0 - 2,8
Be	0,4 - 0,7	0,4 - 0,7
Ni	0,3 max.	*1)
Fe	0,2 max	*1)

kg/dm³	ca. 8,8
Characteristics	CuCo2Be offers a high electrical conductivity and tensile strength and is resistant to high temperatures. CuCo2Be is for instance used for resistance welding. The thermal conductivity at 20 °C is 192 till 239 W/m.K. and the electrical conductivity at 20 °C from 25 till 32 m/ohm.mm².

	EN	DIN
Alloy	CuBe2	CuBe2
Standard	EN 12163, 12165	DIN 17666, 17672
Alloy number	CW101C	2.1247

Chemical composition

Cu	rest	rest
Be	1,8 - 2,1	1,8 - 2,1
Ni	0,3 max.	*1)
Co	0,3 max.	*1)
Fe	0,2 max	*1)

kg/dm³	ca. 8,3
Characteristics	In heat treated condition this alloy contains extremely high mechanical values: hardness and tensile strength. This material is resistant to low temperatures from -200 °C as well as high temperatures till approx. 350 °C. CuBe2 is for instance used for non-sparking and non-magnetic applications and wear resistant parts. The termal conductivity at 20 °C is 92 till 125 W/m.K and the electrical conductivity at 20 °C from 8 till 18 m/ohm .mm².